Preparation and properties of polyurethane coatings modified by polysilazane

Due to their unique physicochemical properties, polysilazanes exhibit excellent performance when combined with some resin matrixes, which had drawn great research attention. In this article, polyurethane (PU) was firstly prepared by polytetrahydrofuran glycol, isophorone diisocyanate, and 1,4-butanediol as main materials. Then, the prepared PU was blended with polysilazane by mixing the two solutions together, which was cured to films via dip-coating method at room temperature. The structure, thermal stability, and surface properties of the composite coatings were investigated by Fourier-transform infrared spectroscopy, thermogravimetric analysis, scanning electron microscopy, and X-ray photoelectron spectroscopy. The results demonstrated that after modification with polysilazane, the heat resistance, hydrophobicity, and mechanical property of the PU coatings were improved. When the content of polysilazane was 6 wt%, the mechanical property of the composite films was optimized, with a maximum tensile strength of 25.7 MPa and elongation at break of 797%. Meanwhile, the water contact angle of the composite film was 107° and the water absorption reached a minimum of 2.1%, which showed improved hydrophobicity and water resistance.