Anticancer and bone-enhanced nano-hydroxyapatite/gelatin/polylactic acid fibrous membrane with dual drug delivery and sequential release for osteosarcoma

Surgical resection of osteosarcoma is always accompanied by residual metastasis of tumor cells and bone tissue defects. In this work, a novel kind of gelatin/polylactic acid (PLA) coaxial fiber membrane with a shell layer containing doxorubicin-loaded hydroxyapatite (DOX@nHAp) nanoparticles and a core layer containing Icariin (ICA) was developed for antitumor and bone enhancement at the defect site. Physical evaluation displayed that the composite membrane provided moderate hydrophilicity, enhanced tensile strength (Dry: 2-3 MPa, wet: 1-2 MPa) and elasticity (70-100 %), as well as increased specific surface area and pore volume (19.39 m2/g and 0.16 cm3/g). In SBF, DOX@nHAp in the fibers promoted biomineralization on the fiber surface. In in vitro evaluation, approximately 80 % of DOX had a short-term release during the first 8 days, followed by long-term release behavior of ICA for up to 40 days. CCK-8 results confirmed that the membrane could actively support MC3T3-E1 cells proliferation and was conductive to high alkaline phosphatase expression, while the viability of MG-63 cells was effectively inhibited to 50 %. Thus, the dual-loaded fibrous membrane with a coaxial structure and nHAp is a promising system for anticancer and defects reconstruction after osteosarcoma surgery.