Hot Compression Deformation Behavior of Mg-Gd-Y-Zn-Zr Alloy

The deformation behaviors of as-cast Mg-11Gd-2Y-Zn-Zr magnesium alloy were investigated by compression test with Gleeble-1500 thermal simulator at temperature of 623-753K and strain rate of 0.01-0.5 s -1 . The flow stress behaviors of the magnesium alloy were carried out at a strain of 0.7. The strain rate and deformation temperature had great influence on the flow stress behaviors. The flow stress increases with increasing strain rate and decreasing temperature. The flow stress has more than one peak stress at a strain rate of 0.5s -1 showing continuous dynamic recrystallization (DRX) mechanism, while other flow stresses exhibited only one peak stress indicating discontinuous dynamic recrystallization (DDRX) mechanism. It was also found that the flow stress behavior could be described by the hyperbolic sine constitutive equation, in which the determined average activation energy is 273.426 kJ·mol -1 . The maximum error value between calculated value and experimental value is 5.5%. The deformation map was also established, and the best parameter for hot working was found to be 0.1s -1 /753k approximately.