Synthesis and photocatalytic degradation activities of phosphorus containing ZnO microparticles under visible light irradiation for water treatment applications

A series of phosphorus containing ZnO (P–ZnO) photocatalysts with various percentages of phosphorus were successfully synthesized using the hydrothermal method. The structural, physical and optical properties of the obtained microparticles were investigated using diverse techniques such as X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, ultraviolet–visible diffusion reflectance spectroscopy (UV–Vis DRS), photoluminescence (PL) spectroscopy, transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDS) and N2 adsorption-desorption analysis. The photocatalytic activities of the pure and P–ZnO samples were evaluated for the degradation of Rhodamine B (RhB) under visible light irradiation. The parameters such as pH, catalyst dosage, contaminant concentration and effect of persulfate as an oxidant were studied. It was found that the P–ZnO1.8% photocatalyst could destroy 99% of RhB (5 ppm) in 180 min at pH = 7; furthermore, it degraded ∼100% of 5 and 10 ppm of the RhB pollutant in 120 and 180 min, respectively, only by adding 0.01 g of persulfate into the reaction solution. To determine the photocatalytic mechanism, 2-propanol, benzoquinone and EDTA were used and it was indicated that hydroxyl radicals, superoxide ions and holes, all had major roles in the photocatalytic degradation but the hydroxyl radical effect was the most significant. The phenol degradation was also investigated using the P–ZnO1.8% optimum photocatalyst which could destroy 53% of the phenol (5 ppm) in 180 min. According to the reusability test, it was proved that after 5 cycles, the catalyst activity was not highly changed and it was potentially capable of pollutant degradation.