Resistance Spot Welding of Dissimilar Alloys 1008 Low Carbon Steel- 1100 Aluminum Alloy

The resistance spot welding is adopted to joint dissimilar alloys such as aluminum alloy 1100 , and low carbon steel alloy 1008 by using cover plate. This study aims to optimization the best conditions of dissimilar welding of Aluminum with low carbon steel by RSW, and improving the properties of joints by many method. three different variables were used for the welding process: welding current (5, 6 ,7 and 8 KA), weld time (0.5, 1 and 1.5 sec) and electrode force (13.2 and 15.5 N).The welding joints are ―examined by a scanning electron microscope SEM and a X-ray diffraction‖ for the purpose of discussing the causes of the improved characteristics. The results revealed that the best welding conditions were under welding current 7 KA , weld time 1 sec and electrode force 13.2 KN, where the joint possessed the maximum shear force (4.8KN) and after improvement the tensile shear force become (6.02 KN), in addition to presence of the intermetallic compounds at optimum condition , such as AlFe3,Al5Fe4 and Al13Fe4, in the joint layer between dissimilar metal improves of the tensile shear forces and hardness in fusion zone.