High content Er3+ doped ZBLAN glass: The spectral characteristics and high slope efficiency MIR laser investigation

The ZBLAN glass with high content of Er3+ was prepared and studied. The glass has a wide infrared transmittance range of 2.5–8.0 µm, which means a lower maximum phonon energy. By testing and analyzing the fluorescence spectrum and lifetime curves under different penetration depths, the intrinsic emission spectrum and lifetime of the sample are obtained without the influence of sub-absorption. Under 980 nm excitation, the maximum emission cross section and the lifetime of 2.7 µm are 6.10 × 10−21 cm2 and 6.49 ms, indicating that high-concentration doping has a larger laser quality factor. According to the rate equation and transmission equation, cascaded and non-cascaded fiber laser models are established to conduct research on 2.7 µm fiber lasers. The slope efficiency can reach 40.38% at a pump wavelength of 980 nm and a fiber background loss of 0.1 dB/m. The high emission cross section, long fluorescence lifetime and high slope efficiency output make ZBLAN glass heavily doped with Er3+ an ideal host material for mid-infrared lasers.