New Formulation of TiO<sub>2</sub>- ZnO Slurry for Facial Foundation Sunscreen Cream Application

The objective of this research was to prepare ready-to-use TiO 2 and ZnO in slurry form for ready-to-use in facial foundation sunscreen. Two types of TiO 2 sources were prepared as TiO2 slurry namely commercial TiO 2 powder and synthesized TiO 2 powder. Preparation of formula 1, 35 g solution PEG-10 dimethicone, and added 20 g solution cyclomethicone after that 45 g TiO2 powder was added slowly to the prepared substance, stirring and heated to 60-70 °C, and stir until the substance mix well. Formula 2, 46 g solution cyclomethicone added 2.5 g stearic acid and 2 g aluminum hydroxide after that stirring and heated to 60-70 °C until the substance mixed well, and TiO 2 powder 49.5 g was added slowly to the continuous stirred and heated. On the other hand, ZnO slurry was prepared in the same steps. The results show that formula 1was the best formulation. Due to it was not precipitation and good compatibility with an emulsifier, therefore, formula 1was chosen to study in various volumes. The texture and stability of the prepared slurry were similar to the commercial slurry. Two sunscreen formulas were differently formulated by containing prepared and commercial slurry and evaluated. There were no significant differences in results between prepared slurry and commercial slurry. To investigate the satisfaction of products, 30 volunteers were asked to use products for one week and answer the questionnaires. The product containing prepared slurry was satisfied by 93.33% of volunteers, whereas the product containing commercial slurry was satisfied by 76.66% of volunteers.