TEMPO/NaBr/NaClO and NaBr/NaClO oxidations of cotton linters and ramie cellulose samples

Dried cotton linters and ramie cellulose samples were oxidized with 2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO)/NaBr/NaClO and NaBr/NaClO (i.e., TEMPO-free) in water at pH 10. The carboxy contents, degrees of polymerization (DPs), X-ray diffraction patterns, and solid-state 13C NMR spectra were measured or obtained for the oxidized products with and without subsequent NaBH4 reduction. Cellulose nanofibrils were prepared from the oxidized cellulose samples by sonication in water and observed by atomic force microscopy and transmission electron microcopy. Because the cellulose molecules were depolymerized with NaBr/NaClO, the depolymerization behavior of the cellulose samples with TEMPO/NaBr/NaClO can be mainly explained by depolymerization with NaBr/NaClO (i.e., not TEMPO-related compounds or reactions). However, because C6-aldehydes formed in the disordered regions periodically present along the longitudinal direction of each cellulose microfibril, the viscosity-average DP values of the TEMPO/NaBr/NaClO-oxidized cellulose samples decreased to 200–300, while those with subsequent NaBH4 reduction exhibited much higher DP values. The nanofibrils prepared from the TEMPO/NaBr/NaClO-oxidized cellulose samples had smallest fibril heights or widths of 5–6 nm. However, significant amounts of unfibrillated bundles with heights of 10–40 mm were present in the nanofibril/water dispersions. The high carboxy contents of the TEMPO/NaBr/NaClO-oxidized cellulose samples (1.62–1.63 mmol/g) indicated that significant amounts of carboxy groups were likely present in the disordered regions, probably forming tail-like polyglucuronate chains. Solid-state 13C NMR analysis revealed that some of the glucosyl units originally with the tg C6–OH conformation were transformed to other conformations by TEMPO/NaBr/NaClO oxidation, while the crystalline C4 signal areas remained constant.