Structural, thermal and optical study of nanocrystalline silicon produced by ball milling

Abstract The ball milling process was used to obtain nanocrystalline cubic silicon. Between 5 and 10 h of milling, amorphous silicon was also formed. The differential scanning calorimetry (DSC) spectrum of a powder milled for 10 h showed that the amorphous–crystalline phase transition occurs at about 450 °C. According to Raman spectroscopy and X‐ray diffraction results, volume fractions of the crystalline, interfacial and amorphous phases were about 30, 39 and 31%, respectively. Copyright © 2010 John Wiley & Sons, Ltd.