GNs/MOF-based mixed matrix membranes for gas separations

NU-1000 and graphene nanosheet (GNs) with different loadings have been used as fillers to prepare mixed matrix membranes (MMMs) with polyethersulfone (PES). The high performance of the MMMs has been successfully fabricated for the evaluation of gas separation at 1 bar and various temperatures (20, 40, 60 °C). The successful fabrication of the MMMs were confirmed by using SEM, FTIR, AFM, and XRD. The crystalline nature of GNs and NU-1000 in the MMMs are evidenced by XRD, which confirms the successful fabrication of the MMMs. In addition, the thermal stability of the MMMs was enhanced with the increase of the GNs. Separation performance of H2 was superior to CO2, N2 and CH4 separation on the MMMs which is a critical for producing energy. The best gas separation results in terms of both permeability and selectivity were obtained with 0.03% GNs and 10% NU-1000. PG3N membrane presented maximum H2/CO2, H2/N2 and H2/CH4 selectivity of 5, 4.2, 3.3 at 20 C, respectively. With an increase in temperature, the permeability increased, while the selectivity of all the MMMs decreased. The MMMs exhibited excellent gas separation capability, which offers unique opportunities for potential large-scale practical applications.