Vyacheslav V. Rodaev,Alexander I. Tyurin,S. S. Razlivalova,V. V. Korenkov,Yuri I. Golovin
出处
期刊:Polymers
[MDPI AG]
日期:2021-11-14
卷期号:13 (22): 3932-3932
标识
DOI:10.3390/polym13223932
摘要
Zirconia nanofiber mats containing filaments with the average diameter of less than 100 nm were fabricated. It is found that the hardness and Young's modulus of the mats are sensitive to the microstructure, phase composition and average diameter of the zirconia nanofibers. The hardness and Young's modulus of the prepared zirconia nanofiber mats vary from 0.86 to 1.67 MPa and from 133 to 362 MPa, respectively, wherein an increase in hardness is accompanied by the rise in Young's modulus.