Effect of gypsum on the hydration and strength development of commercial portland cements containing alkali sulfates

The influence of gypsum content on the hydration and compressive strengths was studied on two commercial Portland cements having the same amount of alite, a similar amount of C3A, but different amounts of readily soluble alkalies and sulfates. The phase analysis of samples hydrated during the 90-days' period was carried out by X-ray diffraction, selective extraction and simultaneous DTA-TG-DTG method. It was observed that all the effects noticed on pure C3S-S-H system are determinant for the optimum gypsum content, although for the sample containing a higher amount of readily soluble alkalies the influence of the added SO3 is considerably modified by the delayed ettringite formation caused by the interaction between Al, Fe-bearing phases and S-rich C-(S,S)-H. Der Einfluss des Gipsgehaltes auf den Hydrationsverlauf und die Druckfestigkeiten der Portlandzemente mit demselben Alitgehalt, ähnlichen C3A-gehalt und verschiedenen Gehalt an schnell-löslichen Alkalien und Sulfaten wurde studiert. Eine Untersuchung des Hydratationsprocesses mittels Rö-beugung, DTA-TG-DTG und der Extraktionsmethode wurde durchgefuehrt. Man hat festgestellt, dass alle an C3S-S-H Mischungen beobachteten Effekte für den günstigsten Gipszustatz entscheidend sind; in Falle des Klinkers mit einem höheren R2O-gehalt wurden jedoch diese Effekte durch eine spätere Ettringitbildung modifiziert.