Synergistic Flame-Retardant Effect of Aluminum Diethyl Phosphinate in PP/IFR System and the Flame-Retardant Mechanism

Abstract Synergistic flame-retardant effect of aluminum diethyl phosphinate (AlPi) in intumescent flame retardant polypropylene (PP/IFR) system and the flame-retardant mechanism were investigated. The flame retardancy of PP/IFR/AlPi (the mass ratio of IFR to AlPi is 2 : 1) was the best, which was proved by the results of the limiting oxygen index (LOI) test, UL-94 test, and cone calorimeter test ( CCT) test. Here, the LOI value of the sample was as high as 34% and passed the V–0 rating in UL–94 test. The peak heat release rate (PHRR) decreased by 92.57%, the total heat release (THR) reduced by 90.52%. Thermogravimetric (TGA) data showed that the introduction of AlPi improved thermal stability and changed the thermal degradation behavior of PP/IFR composites. Interestingly, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDXS) and laser Raman spectroscopy (LRS) proved that PP/IFR/AlPi had formed more residual carbon, but the flame retardancy was worse than PP/IFR/AlPi. This is because when the mass ratio of IFR to AlPi is 2 : 1, the synergy between IFR and AlPi was significant, gas-phase flame retardant and condensed-phase flame retardant reached a balance and obtained the best flame retardant effect.