Swelling behaviour of a new kind of polyampholyte hydrogel composed of dimethylaminoethyl methacrylate and acrylic acid

Abstract Poly[(dimethylaminoethyl methacrylate)‐ co ‐(acrylic acid)] [poly(DMAEMA‐ co ‐AAc)] hydrogels have been synthesized by UV‐induced copolymerization of dimethylaminoethyl methacrylate (DMAEMA) and acrylic acid monomer. The effects of pH and ionic strength on the swelling behaviour of poly(DMAEMA‐ co ‐AAc) hydrogels were investigated in detail. It was found that there is minimal equilibrium swelling ratio (ESR) for the hydrogels with the change of pH, and the pH at minimal ESR of the hydrogels was defined by the isoelectric points (IEP), similar to the situation with protein molecules. The IEP of the hydrogels shifted to higher values with increase in the DMAEMA content in the hydrogels. Antipolyelectrolyte behaviour of the hydrogels at a pH near the IEP was observed as well, and the ESR increased with increasing ionic strength. The study of swelling kinetics of the hydrogels showed that the swelling process was Fickian at the IEP and non‐Fickian when the pH deviated from the IEP. Copyright © 2003 Society of Chemical Industry