Fire-Resistant and Thermal Stability Properties of Fluorosilicone Adhesives by Incorporation of Surface-Modified Aluminum Trihydrate

Fluorosilicone was combined with aluminum trihydrate (ATH) to induce synergistic flame-retardant and thermal-resistant properties. The surface of ATH was modified with four different silane coupling agents. The flammability and mechanical properties of the fluorosilicone/ATH composites were assessed using an UL94 vertical test and a die shear strength test. The change in shear strength was investigated under aging for 1000 h at −55 °C and 150 °C. Pure fluorosilicone had inherent fire resistance and thus achieved a V-0 rating even at 20 wt.% ATH loading. Upon addition of ATH treated with 3-glycidoxypropyl trimethoxysilane, the composites exhibited the highest shear strength of 3.9 MPa at 23 °C because of the additional crosslinking reaction of fluorosilicone resin with the epoxide functional group of the coupling agent. Regardless of the types of coupling agents, the composites exhibited similar flame retardancy at the same ATH content, with a slight reduction in shear strength at 180 °C and 250 °C. The shear strength of the adhesives gradually decreased with aging time at −55 °C, but increased noticeably from 3.9 MPa to 11.5 MPa when aged at 150 °C due to the occurrence of the additional crosslinking reaction of fluorosilicone.