Thermal, chemical, and mechanical properties of niobium phosphate glasses and glass-ceramics

In this work, glass samples were obtained by melt-quenching in the binary system (100-x)KPO3-xNb2O5 with x = 20, 30, 40, and 50 mol%. Thermal properties investigated by DSC together with structural investigations by Raman spectroscopy allowed to understand the structural effect of Nb2O5 incorporation in the potassium phosphate glass network. A transparent glass-ceramic has also been produced by heat treatment of the 50KPO3–50Nb2O5 glass sample. Density, molar volume, atomic packing, and refractive index were determined and increased with Nb2O5 content. Chemical resistance in several corrosive aqueous solutions was found to increase with Nb2O5 content and crystallization. Vickers hardness as well as elastic modulus and hardness obtained from nanoindentation experiments also strongly increased with higher niobium contents, indicating that not only optical properties but also chemical and mechanical properties are improved with niobium incorporation in the phosphate glass network.