Thermal Degradation Behavior of Hydrogen Permeability of Pd-Coated V-Alloy Membrane for Hydrogen Separation and Purification

A series of accelerated degradation experiments at high temperatures have been performed for Pd-coated V-10 mol% Fe alloy membranes in order to investigate the degradation behavior of hydrogen permeability. The degradation of the membrane becomes severer with increasing testing temperature. The temperature dependence of the 20% degradation rate almost obeys the Arrhenius relationship, suggesting that the degradation phenomenon occurs by a kind of thermal activation process. It is found that the addition of a small amount of W into Pd overlayer improves the durability of the membrane significantly.