Investigating the effect of zirconium‐based and titanium‐based metal–organic frameworks nanoparticles on the performance of polysulfone hollow fiber mixed matrix membrane for dialysis application

Abstract This study aims to investigate polysulfone (PSF) mixed matrix membranes (MMMs) properties containing zirconium‐based and titanium‐based metal–organic frameworks (MOFs). for hemodialysis application. The nanoparticles were synthesized, and the membranes were produced by the phase inversion method. Membrane characterization conducted by attenuated total reflection Fourier transform infrared spectroscopy (ATR‐FTIR), field emission Scanning electron microscope (FE‐SEM), energy‐dispersive x‐ray analysis (EDX), transmission electron microscopy (TEM), x‐ray diffraction (XRD), and atomic force microscopy (AFM) confirmed the presence of MOF nanoparticles. Also, the evaluation of the specific surface area of nanoparticles was done by BET. The water contact angle reduced from 64.4° to 51.2°, indicating the hydrophilicity improvement, enhancing the pure water flux from 46.8 L/m 2 h for the pristine membrane to 76.7 L/m2h for the pristine membrane M 4 . The total fouling resistance decreased from 30% to 21%, and the bovine serum albumin (BSA) adsorption of modified membranes was lower than that of the pristine membrane. Urea and creatinine were cleared significantly for modified ones, up to 82.6% and 72.1%, respectively, and all membranes showed BSA retention of more than 93%. A comparison between MMMs that contained UIO‐66‐NH 2 and MIL‐125‐NH 2 showed that the former had a better effect on the performance. M 4 had better results, indicating high water flux, the lowest fouling resistance, high porosity, lower BSA adsorption, proper clearance for urea and creatinine, and 94.2% BSA retention.