Effect of Thermomechanical Loading on the Cementation Interface of Implant-Supported CAD/CAM Crowns Luted to Titanium Abutments

Purpose To investigate the effect of aging on the morphology of the interface between monolithic implant crowns and standardized titanium base abutments. Materials and methods Four groups of hybrid abutment crowns differing in restorative material (lithium disilicate [LD] or polymer-infiltrated ceramic network [PICN]) and in fabrication procedure of the interfacial zone for luting to a titanium abutment (milled during CAD/ CAM procedure [M] or prefabricated [P]) were formed: LDS-M, LDS-P, PICN-M, and PICN-P (n = 10 each). The morphology of the crown-abutment interface was examined before and after artificial aging using scanning electron microscopy. The total gap length per specimen was measured at both time points, and intergroup (Kruskal-Wallis [KW]) plus pairwise (Wilcoxon Mann-Whitney [WMW]) comparisons were performed (α = .05). Results Before aging, statistically significant differences in gap length were identified among groups (KW: P = .0369) for PICN-P > LDS-P (WMW: P = .0496) and LDS-M > LDS-P (WMW: P = .0060). The effect of aging among the groups, expressed as an increment of total gap length, was 50% in LDS-M, 30% in LDS-P, 20% in PICN-M, and 30% in PICN-P. After aging, the statistically significant differences in gap length identified among groups (KW: P = .0048) were for PICN-P > LDS-P (WMW: P = .0134); LDS-M > PICN-M (WMW: P = .0204); PICN-P > PICN-M (WMW: P = .0486); and LDS-M > LDS-P (P = .0022). However, comparison of the difference in gap length from before to after aging among the groups was not statistically significant (KW: P = .3549). Conclusion The cementation interfaces of CAD/CAM crowns on standardized titanium base abutments demonstrated a high percentage of gaps before and after thermomechanical loading. The composition of the restorative material and the nature of the interface influenced the interfacial gap dimension.