Porous boron nitride intercalated zero-valent iron particles for highly efficient elimination of organic contaminants and Cr (VI)

Developing novel bifunctional materials to high efficiently degrade organic pollutants and eliminate hexavalent chromium (Cr (VI)) is significantly desired in the wastewater treatment field. The porous boron nitride (p-BN) was fabricated by a two-stage calcination strategy and was innovatively employed to support zero-valent iron (ZVI), achieving the bifunctional material (p-BN@ZVI) to degrade carbamazepine (CBZ) and eliminate Cr (VI). p-BN@ZVI could degrade more than 98% CBZ in 6 min with the high apparent first-order constant (kobs) of 0.536 min-1, almost 5 times higher than that of the ZVI/PMS system and outperformed most previous reported ZVI supported catalysts, which was mainly ascribed to the fact that the introduction of p-BN with high surface area (793.97 m2/g) improved the dispersion of ZVI and exposed more active sites. Quenching tests coupled with electron paramagnetic resonance (EPR) suggested that •OH was the major reactive oxygen species with a contribution of 71.6%. Notably, the p-BN@ZVI/PMS system expressed low activation energy of 8.23 kJ/mol and reached a 65.69% TOC degradation in 20 min even at 0 °C. p-BN@ZVI possessed remarkable storage stability and could still degrade 92.3% CBZ despite three-month storage. More interestingly, p-BN@ZVI was capable to eliminate 98.1% of 50 mg/L Cr (VI) within 5 min through adsorption and reduction, where nearly 80% Cr (VI) was transformed to Cr (III), and exhibited the maximum Cr (VI) elimination capacity of 349 mg/g. This study provides new insights into the efficient organic contaminants degradation and Cr (VI) elimination in the treatment of wastewater.