J. Bukowski,S. Brunner
标识
DOI:10.1016/0008-8846(79)90095-4
摘要
Carbonation of non-hydraulic, γ-Ca2SiO4 and CaSiO3, mortars and powders exposed to 100% RH and 100% CO2 environments were studied. The rate of reaction and strength development is faster in γ-Ca2SiO4 than in CaSiO3. Increasing CO2 pressure from atmospheric to 5.62 MPa increases the degree of reaction in both γ-Ca2SiO4 and CaSiO3. Strength increases as a function of degree of reaction and CO2 pressures above 2.00 MPa. The potential use of non-hydraulic materials for CO2 activated cements is discussed. Karbonatisering af “non-hydraulic” calcium silikater, γ-Ca2SiO4 og CaSiO3 som mørtler og “powders” udsat for 100% relative fugtighed og 100% CO2 omgivelser blev studeret. Reaktionshastigheden og styrkeudviklingen er hurtigere i γ-Ca2SiO4 end i CaSiO3. Tiltagende CO2 tryk fra atmosfaerretryk op til 5.62 MPa øger reaktionsgraden i både γ-Ca2SiO4 og CaSiO3. Styrke tiltager som funktion af karbonatiseringsgraden og CO2 tryk undtagen i γ-Ca2SiO4 ved CO2 tryk over 2.00 MPa. Den potentielle nytte ved “non-hydraulic” materialer aktiveret til cement, ved hjaelp of CO2, er diskuteret.
科研通智能强力驱动
Strongly Powered by AbleSci AI