Intense red up-conversion luminescence and temperature sensing property of Yb3+/Er3+ co-doped BaGd2O4 phosphors

In this study, intense red and extremely weak green up-conversion (UC) luminescence was obtained in BaGd2O4: x mol% Yb3+/y mol% Er3+ phosphors under the excitations of 980 nm and 1550 nm. The corresponding maximum integrated intensity ratios of the red to green UC emissions are 50.3 and 158.7, respectively. The UC luminescence mechanisms upon different excitations were discussed. It was confirmed that two-photon and three-photon processes were responsible for both the red and green UC emissions excited at 980 nm and 1550 nm, respectively. The energy transfer efficiency from Er3+ to Yb3+ was calculated according to the fluorescence lifetime measurement under 1550 nm excitation. Temperature sensing based upon the thermally coupled energy levels 2H11/2/4S3/2 as well as thermally coupled Stark sublevels of 4F9/2 level of Er3+ was investigated under the excitation of 980 nm. The maximum absolute sensitivities were respectively obtained to be 0.42% K-1 at 573 K and 0.18% K-1 at 298 K. Our results indicated that BaGd2O4: Yb3+/Er3+ phosphors might be a kind of promising red UC phosphors with optical temperature measurement function.