Influence of oriented β‐lamellae on deformation and pore formation in β‐nucleated polypropylene

ABSTRACT Four β‐nucleated polypropylene samples with increasing die draw ratio (DDR) were prepared to modify lamellae arrangement. The DSC, SEM, and 2D‐XRD results show that all four cast films had similar crystallinity, high contents of β‐crystal but lowering stability of β‐lamellae with ascending DDR. Meanwhile, the anisotropy of β‐lamellae distribution strengthens gently and the stacked lamellae structure perpendicular to the machine direction (MD) predominates dramatically. Tensile testing at 25 °C and 90 °C were conducted along MD and transverse direction (TD), respectively. The markedly expanding difference of deformation indicates the anisotropy highlighted significantly. Additionally, when the samples stretched along MD, a more homogeneous deformation occurs with ascending anisotropy, which is completely opposite to the β‐lamellae stability. But samples deformed more heterogeneous when stretched along TD. The characterization of morphological evolutions during stretching shows that the stacked lamellae debonds uniformly and abundant microvoids formed when the sample stretched along MD with higher anisotropy, resulting in evenly dispersion of stress, consequently making a more uniform distribution of defects and a better isotropic deformation. Moreover, the microfibrils and defects distributed uniformly within higher orientation sample after longitudinal stretching stretched along MD, leading to the dramatic improvement of pore size distribution of the membrane after biaxial stretching. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2017 , 55 , 1745–1759