Enhanced Interfacial Properties of Carbon Fiber/Polymerization of Monomers Reactants Method Polyimide Composite by Polyimide Sizing

Carbon fiber (CF)-reinforced polyimide (PI) resin matrix composites have great application potential in areas such as rail transport, medical devices, and aerospace due to their excellent thermal stability, dielectric properties, solvent resistance, and mechanical properties. However, the epoxy sizing agent used for traditional carbon fiber cannot withstand the processing temperature of polyimide resin, of up to 350 °C, resulting in the formation of pores or defects at the interface between the fiber and the resin matrix, leading to the degradation of the overall composite properties. To overcome this problem, in this study, a low-molecular-weight thermosetting polyimide sizing agent was prepared and the processability of the sized carbon fiber was optimized by a thermoplastic polyimide. Compared with the unsized carbon fiber polyimide composites, the interfacial properties of the composites after the polyimide sizing treatment were significantly improved, with the interfacial shear strength (IFSS) increasing from 82.08 MPa to 136.27 MPa, the interlaminar shear strength (ILSS) increasing from 103.7 to 124.9 MPa, and the bending strength increasing from 2262.2 MPa to 2562.1 MPa. The sizing agent acts as a bridge between the carbon fiber and polyimide resin, with anchorage and bonding at the interface between the fiber and resin, which are beneficial for enhancing the interface performance of composites.