Synthesis, characterization, and cure properties of phosphorus-containing epoxy resins for flame retardance

An organophosphorus compound, 10-(2,5-dihydroxyl phenyl)-9, 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DHPDOPO), was synthesized through the reaction of 9,10-dihydro-9-oxa-10-phosphaphnanthrene-10-oxide (DOPO) and p-benzoquinone, and characterized by elemental analysis, Fourier transform infrared spectrum (FTIR), and 1H-NMR and 31P-NMR spectroscopes. Consequently, the phosphorus-containing epoxy resins with phosphorus content of 1 and 2 wt.% were prepared via the reaction of diglycidyl ether of bisphenol-A with DHPDOPO and bisphenol-A, and confirmed with FTIR and gel permeation chromatography (GPC). Phenolic melamine, novolak, and dicyanodiamide (DICY) were used as curing agents to prepare the thermosetted resins with the control and the phosphorus-containing epoxy resins. Thermal properties and thermal degradation behaviors of these the thermosetted resins were investigated by using differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Phenolic melamine-cured resins exhibited higher glass transition temperatures than the other cured resins due to the high rigidity of their molecular chain. TGA studies demonstrated that the decomposition temperatures of the novolak-cured resins were higher than those of the others. A synergistic effect from the combination of the phosphorus-containing epoxy resin and the nitrogen-containing curing agent can result in a great improvement of the flame retardance for their thermosetted resins.