Synthesis, growth, optical, mechanical, thermal, dielectric, and SHG properties of Triethylaminium picrate (TEAP) single crystal for nonlinear optical applications

Triethylaminium picrate (TEAP) crystals were grown using the slow evaporation solution growth method at ambient (35 °C) temperature. Salt was synthesized from Picric acid, and Triethylamine and methanol was used as solvents. The solution was mixed at a 1:1 ratio and evaporated slowly, produced yellow colour single crystal of TEAP with an average dimension of 19 × 8 × 5 mm3. The structure of the compound was determined by single-crystal X-ray diffraction (SCXRD) study, which confirms that the crystal is belongs to Orthorhombic crystal system, and its crystallinity was confirmed by the Bragg peak in the powder X-ray diffraction pattern. The superamolecular characteristic of the TEAP was confirmed by the Hirshfield analysis. CHN elemental analysis confirmed the stoichiometry and chemical composition of the synthesized complex salts. FT-IR and Polarized Raman spectral analyses confirmed the presence of different functional groups in the complex. UV–vis–NIR study identified the optical transmission window and the lower (TEAP) cut-off wavelength. Vickers' microhardness analysis determined the mechanical stability of the grown crystal. Studies of dielectric and AC conductivity were analyzed as a function of frequency. The thermogravimetry (TG) and differential thermal analysis (DTA) techniques were used to investigate the thermal behaviour of the material. The Kurtz-Perry powder technique was used to analyze the crystal's nonlinear optical properties (NLO) and found that its SHG efficiency was 1.5 times higher than that of potassium dihydrogen phosphate (KDP). The results from the obtained characterizations conclude that the TEAP crystal could be useful for NLO applications.