Effect of Heat Treatment on Microstructure and Mechanical Properties of Titanium Alloy Fabricated by Laser–Arc Hybrid Additive Manufacturing

The tailored thermal heat-treatment process for Ti-6Al-4V alloy manufactured by laser–arc hybrid additive manufacturing can achieve desired microstructures and excellent mechanical properties for components. The effects of different heat treatment regimens on the microstructure and mechanical properties of Ti-6Al-4V alloy manufactured by laser–arc hybrid additive manufacturing are investigated in this study. Utilizing optical microscopy and scanning electron microscopy, we analyze the variations in microstructure with changes in heat-treatment parameters and explore the reasons for the changes in mechanical properties under different solutions’ treatment temperatures and cooling rates. The microstructure of Ti-6Al-4V alloy fabricated via laser–arc hybrid additive manufacturing was primarily composed of Widmanstätten α plate structures and a small amount of acicular martensite α′ within columnar β grains that grew outward from the substrate along the deposition direction. Following solution treatment and aging heat treatment, the microstructure transitioned to a typical high-performance net basket structure with significantly reduced α plate thickness, leading to noticeable enhancements in sample ductility and toughness. Specifically, when the solution treatment and aging treatment regimen was set at 950 °C for 1 h, followed by air cooling, and then aging at 540 °C for 6 h with subsequent air cooling, the average grain size decreased by a factor of two compared to the as-deposited samples, while the impact toughness increased by 66.7%.