Bio-based aerogel composites of coconut pith-derived carbon and chitosan for efficient anionic dye-polluted water treatment

Abstract Biomass-based aerogels are of interest due to their abundant precursors, ease of functionalization, eco-friendliness, low cost, and effectiveness in dye-contaminated water treatment. Coconut pith (CP) known as a by-product after coconut processing is a sponge-like and lightweight material discarded in large volumes. For the first time, carbon micro-particles resulting from two-step treatment and pyrolysis of CP have been successfully incorporated with chitosan to produce aerogel composites by high-speed homogenization and freeze-drying. After pretreatment, holocellulose content and crystallinity index of the recovered CP pulp are respectively 75.4 and 58.6 % along with a solid recovery rate of 27.5 %. Characteristic properties of the aerogel composites are featured by their density as low as 15.23–28.17 mg/cm 3 , remarkably high porosity of 98.17–99.05 %, and Young’s modulus of 1.64–12.23 kPa. Synergistic effects of the porous network, electrostatic interactions between both amine groups in chitosan and carbon surface with methyl orange (MO) cause the as-fabricated aerogel composites to achieve an extremely high adsorption capacity of 454.13 mg/g and removal efficiency of 92.32 % at initial MO concentration of 500 mg/L. Therefore, the CP-derived carbon/chitosan aerogel composites synthesized from a feasible procedure exhibit their great potential in enhancing the value of coconut waste and dealing with dye-contaminated water pollution by simple and economical adsorption.