Action of triethanolamine on the hydration of tricalcium aluminate

Hydration characteristics of tricalcium aluminate and tricalcium aluminate + gypsum were studied following addition of 0.5, 1.0, 5.0 or 10.0% triethanolamine (TEA) at a solution/C3A ratio of 1.0 after hydration periods of 1 to 60 min. TEA accelerated the hydration of C3A to the hexagonal aluminate hydrate and its conversion to the cubic aluminate hydrate. The rate of hydration increased with increased amounts of TEA, which also accelerated the formation of ettringite in the C3A-gypsum-H2O system. Les caractéristiques d'hydratation de l'aluminate de tricalcium et de l'aluminate de tricalcium + gypse ont été étudiées après l'addition de 0.5, 1.0, 5.0 ou 10% de triéthanolamine (TEA) dans un rapport solution/C3A de 1.0 après de périodes d'hydratation allant de l à 60 min. La TEA accélère l'hydratation du C3A en hydrate d'aluminate hexagonal et sa conversion en hydrate d'aluminate cubique. La vitesse d'hydration augmente en proportion directe de la quantité de TEA, qui accélère également la formation de l'ettringite dans le système C3A-gypse-H2O.