Wettability Alteration of Dolomite Rock Using Nanofluids for Enhanced Oil Recovery

Wettability alteration of rock by surfactant has been considered as feasible method for recovery of oil reservoirs by modifying the wettability of rock surface from oil-wet to water-wet condition. The impact of surfactant can be enhanced by adding nanoparticles. Cationic surfactant performed well in carbonate rock by forming ion pairs between cationic head and acidic component of the crude. Meanwhile, nanoparticles will form continuous wedge film between the liquid and solid surface. In this paper, Al 2 O 3 and ZrO 2 nanoparticles were used as enhanced oil recovery (EOR) agents. The impact of these two nanoparticles on contact angle and interfacial tension was studied. Besides that, adsorption Cetyltrimethylammonium Bromide (CTAB) surfactant on rock surface was also investigated. The results show a significant change in water-oil contact angle after application of surfactant and nanoparticles. Initial water-oil contact angle for 6 dolomites demonstrate oil-wet condition. Then, the dolomites were submerged in prepared solution for 48 hours. The result shows that, dolomites 2, 5 and 6 changes drastically to more water-wet condition with contact angle 56°, 40° and 47° respectively. For surfactant adsorption, the adsorption is very fast at the beginning. The adsorption rate after 5 minutes was 50 mg/g and after 60 minutes the adsorption rate was 310 mg/g. The adsorption rate slowed down after 60 minutes and after 180 minutes the adsorption rate was 315 mg/g in which the rate of adsorption achieve equilibrium. Nanoparticles retention test and Zeta potential shows that Al 2 O 3 is more stable than ZrO 2 . The results for interfacial tension (IFT) also show a significant reduction. The IFT value reduces from 8.46 mN/m to 1.65 mN/m and 1.85 mN/m after the application of Al 2 O 3 and ZrO 2 nanofluids respectively