Mechanical properties and microstructure evolution of MgO–Al–C slide plate refractories in presence of Al powder-modified magnesia aggregates

MgO–Al–C slide plate refractories were fabricated using sintered magnesia and modified sintered magnesia as aggregates, fused magnesia aggregates and fines, Al powder and carbon black (N220) as fines, and thermosetting phenolic resin as the binder. Al powder-modified magnesia aggregates were prepared and characterized and were introduced into the MgO–Al–C slide plate refractories. The effects of the modified aggregates on the properties, phase composition, and microstructure were investigated. 1) The Al powder-modified magnesia aggregates exhibited considerably high bonding strengths and low Al powder shedding ratios, thus meeting the preparation requirements of MgO–Al–C slide plate refractories. 2) At high temperatures, more needle-like and fibrous Al 4 C 3 , AlN and octahedral MgAl 2 O 4 were generated on the surface of the modified magnesia aggregates, which enhanced the bond between the matrix and the aggregates and increased the hot modulus of rupture of the material. 3) Non-oxide Al 4 C 3 and AlN phases were formed in situ and had high thermal conductivity and low coefficient of expansion; this could relieve the internal thermal stress of the material and create a toughening effect, improving the thermal shock resistance of the material.