A Photoluminescence Study of Eu3+, Tb3+, Ce3+ Emission in Doped Crystals of Strontium-Barium Fluoride Borate Solid Solution Ba4−xSr3+x(BO3)4−yF2+3y (BSBF)

The present study is aimed at unveiling the luminescence potential of Ba4-xSr3+x(BO3)4-yF2+3y (BSBF) crystals doped with Eu3+, Tb3+, and Ce3+. Owing to the incongruent melting character of the phase, the NaF compound was used as a solvent for BSBF crystal growth. The structure of BSBF: Eu3+ with Eu2O3 concentration of about 0.7(3) wt% was solved in the non-centrosymmetric point group P63mc. The presence of Eu2O3 in BSBF: Eu3+ leads to a shift of the absorption edge from 225 nm to 320 nm. The photoluminescence properties of the BSBF: Ce3+, BSBF: Tb3+, BSBF: Eu3+, and BSBF: Eu3+, Tb3+, Ce3+ crystals have been studied. The unusual feature of europium emission in BSBF is the intensively manifested 5D0→7F0 transition at about 574 nm, which is the strongest for BSBF: Eu3+ at 370 nm excitation and for BSBF: Eu3+, Tb3+, Ce3+ at 300 nm and 370 nm excitations. No evidence of Tb3+→Eu3+ energy transfer was found for BSBF: Eu3+, Tb3+, Ce3+. The PL spectra of BSBF: Eu3+ at 77 and 300 K are similar with CIE chromaticity coordinates of (0.617; 0.378) at 300 nm excitation and (0.634; 0.359) at 395 nm excitation and low correlated color temperature which implies application prospects in the field of lightning. Due to the high intensity of 5D0→7F0 Eu3+ transition at 370 nm excitation, the BSBF: Eu3+ emission is yellow-shifted.