Ein Beitrag zur Kristallstruktur von Ba2ScAlO5 und Sr2Sc0,5Al1,5O5

Single crystals of (I) Ba2ScAlO5 and (II) Sr2Sc0.5Al1.5O5 were prepared by high temperature reactions and investigated by the X-ray technique. (I) belongs to the BaTiO3 type (a = 5.7965 Å; c = 14.5398 Å; space group, D6h4 (P63/mmc); Z = 3) and (II) show a cubic perovskite structure (a = 7.9078 Å; space group, Th6(Pa3); Z = 4). The reinvestigation of (I) shows only one underoccupied point position of O(2). The substitution of Ba2+ by Sr2+ changes the 6L-type structure of (I) to the classic cubic perovskite with partially ordered occupation of octahedra holes of (II). Einkristalle von (I) Ba2ScAlO2 und (II) Sr2Sc0,5Al1,5O5 wurden durch Hochtemperaturreaktionen erhalten und röntgenographisch untersucht. (I) kristallisiert im hexagonalen BaTiO3-Typ (a = 5,7965 Å; c = 14,5398 Å; Raumgruppe, D6h4 (P63/mmc); Z = 3). (II) kristallisiert in einer kubischen Perowskitstruktur (a = 7,9078 Å; Raumgruppe, Th6(Pa3); Z = 4). Die Nachuntersuchung von (I) zeigt im Gegansatz zur bisherigen Auffassung nur eine unterbesetzte Punktlage für O(2). Der Austausch von Ba2+ durch Sr2+ verändert die 6L-Struktur von (I) zum klassischen kubischen Perowskit mit partiell geordneter Besetzung der Oktaederlücken in (II).