Electrically conductive poly(3,4‐ethylenedioxythiophene)–polystyrene sulfonic acid/polyacrylonitrile composite fibers prepared by wet spinning

Abstract Composite conductive fibers based on poly(3,4‐ethylenedioxythiophene) (PEDOT)–polystyrene sulfonic acid (PSS) blended with polyacrylonitrile (PAN) were prepared via a conventional wet‐spinning process. The influences of the PEDOT–PSS content on the electrical conductivity, thermal stability, and mechanical properties of the composite fibers were investigated. The fibers with 1.83 wt % PEDOT–PSS showed a conductivity of 5.0 S/cm. The breaking strength of the fibers was in the range 0.36–0.60 cN/dtex. The thermal stability of the PEDOT–PSS/PAN composite fibers was similar to but slightly lower than that of the pure PAN. The X‐ray diffraction results revealed that both the pure PAN and PEDOT–PSS/PAN composite fibers were amorphous in phase, and the crystallization of the latter was lower than that of the former. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013