Gradient HfB2-SiC multilayer oxidation resistant coating for C/C composites

The gradient HfB2 modified SiC coating was prepared on the surface of SiC-coated C/C composites by in-situ synthesis. Anti-oxidation behaviors of the coated C/C samples at 1773, 1873 and 1973 K were investigated. The results show that the gradient HfB2 modified SiC coatings possess excellent oxidation resistance, which can protect C/C substrates from oxidation for 800, 305 and 100 h at 1773, 1873 and 1973 K, respectively. In addition, with the oxidation temperature increasing, the evaporation of the Hf-Si-O glass layer and the active oxidation of SiC were accelerated, which is the reason for the worst oxidation resistance of the sample at 1973 K among the three temperatures.