Preparation and Enzyme Degradability of Spherical and Water-Absorbent Gels from Sodium Carboxymethyl Cellulose

To synthesize a biodegradable alternative to spherical polyacrylic acid absorbent resin, spherical hydrogel particles were prepared from carboxymethyl cellulose (CMC) dissolved in an aqueous solution, using ethylene glycol diglycidyl ether (EGDE) as a crosslinking agent. The effect of varying the initial CMC concentration and feed amount of EGDE on the shape, water absorbency, water-holding capacity, and enzyme degradability of the resultant CMC hydrogels was determined. The reaction solution was poured into fluid paraffin, and spherical hydrogel particles were obtained via the shear force from stirring. The shape and diameter of the spherical hydrogel particles in the swollen state depended on the CMC concentration. The spherical hydrogel particles obtained by increasing the amount of EGDE resulted in a decrease in absorbency. Additionally, all the spherical hydrogel particles were degraded by cellulase. Thus, spherical biodegradable hydrogel particles were prepared from CMC, and the particle size and water absorption of the hydrogel could be controlled in the range of 5-18 mm and 30-90 g·g-1 in the swollen state, respectively. As an alternative to conventional superabsorbent polymers, the spherical CMC hydrogels are likely to be useful in industrial and agricultural applications.