Preparation and water erosion resistance properties of tara gum-g-poly (acrylic acid-co-methyl methacrylate) emulsion

The main purpose of this paper is to synthesize a new kind of green and environmental protection emulsion, which can be used as water erosion resistant materials. Here, a non-toxic polymer was prepared by grafting acrylic acid (AA) and methyl methacrylate (MMA) onto the long chains of tara gum (TG) to synthesize a copolymer emulsion (TG-g-P (AA-co-MMA)). The structure, thermal stability, morphology and wettability of the polymer were characterized by conventional methods, and the effects of key synthesis conditions on the performance of the emulsion (viscosity) were optimized. The erosion resistance and compressive strength of polymer-treated loess and laterite soils were evaluated under laboratory conditions. The results showed that the successful grafting of AA and MMA monomers onto TG improved its thermal stability and viscosity. In soil performance tests with low amounts of polymer additive, a 0.3 wt% application of TG-g-P (AA-co-MMA) to loess could resist continuous precipitation for >30 h with an erosion rate of 2.0 %. The compressive strength of the laterite treated with 0.4 % TG-g-P (AA-co-MMA) was 3.7 MPa, which was about three times that of the untreated soil. The results from this study suggest that TG-g-P (AA-co-MMA) emulsions have good potential for soil remediation applications.