Mouna Rafei,Xiuyu Wu,Alexis Piñeiro García,Vladimir Miranda La Hera,Thomas Wågberg,Eduardo Gracia‐Espino
标识
DOI:10.1002/admi.202201214
摘要
Abstract Solution precursor plasma spraying is used to produce catalytic trimetallic coatings containing Ni, Fe and Mo directly onto stainless‐steel mesh, Ni foam and carbon paper. The resulting material is mostly comprised of face centered cubic FeNi 3 alloy forming a highly porous coating with nanostructured features. The addition of Mo (up to ≈14 at%) generates no new crystal phases but only an increase in the lattice parameter, indicating the formation of FeNi 3 Mo x solid solutions. The FeNi 3 Mo x solid solutions are used as electrocatalyst for the hydrogen evolution reaction (HER) in alkaline media. The addition of Mo increases the HER activity significantly reaching an optimum performance at ≈9 at% Mo (FeNi 3 Mo 0.40 ) with an overpotential at −10 mA cm −2 of 112 mV and a Tafel slope of 109 mV dec −1 . The enhanced HER activity is attributed to the formation of a FeNi 3 Mo x solid solution with an increased work function that is correlated to smaller hydrogen adsorption energies. Theoretical activity maps reveal that sites near superficial Mo atoms forms catalytic hot spots and are responsible for the observed activity.
科研通智能强力驱动
Strongly Powered by AbleSci AI