Growth of AlGaN alloys with ∼ 90 % AlN mole fraction by plasma-assisted molecular beam epitaxy: Indication of phase-segregation effects

AlGaN alloys with very high AlN mole fraction (∼90 %) were grown by plasma-assisted molecular beam epitaxy (PA-MBE) and their alloy properties were investigated by high-resolution X-ray diffraction (HR-XRD) measurements. Growth was carried out employing a series of group III/V ratios and for samples grown under a high group-III regime, phase-segregation in the alloy was evident from a characteristic splitting of the AlGaN (0002) peak in the HR-XRD pattern. With decreasing excess group-III conditions the separation of peak positions continuously reduced, till a single peak was observed. However, for samples where such splitting was absent, spontaneous superlattice peaks were seen at lower incident angles of the XRD patterns indicating the presence of long-range atomic ordering (LRAO). Thus, for AlGaN alloys with extremely high Al content, effects of phase-segregation, or of LRAO were observed, depending on the kinetics of growth. These results on phase-segregation effects are expected to promote the development of high-efficiency deep ultraviolet emitters for skin-safe germicidal action by mitigating the detrimental effect of dislocations and related non-radiative recombination centers through carrier localization processes at potential minima.