Lightweight Through-Hole Copper Foil as a Current Collector for Lithium-Ion Batteries

In the past few decades, much effort has been dedicated to improve electrochemical performance of lithium-ion batteries (LIBs) through material design. Less attention, however, has been paid to structure engineering of battery components, which is an effective way for improving the electrochemical performance of LIBs. In this work, a lightweight Cu current collector with a through-hole array and columnar crystal on the surface (CC/THCu) was designed and fabricated using a nanosecond ultraviolet laser and electrodeposition processing to enhance specific capacity and cycle stability of LIBs. The synergistic effect of the columnar crystal and through-hole structure for improving electrochemical performances of LIBs assembled with the CC/THCu current collector was investigated. The results show that the complex structure provides spaces for volume expansion and reduces volume variation. When the hole fraction reaches 20%, the weight loss of CC/THCu is 28.41%. The corresponding LIB with the 20% hole fraction CC/THCu shows a high residual capacity rate of 81.2% and enhanced specific capacity (55.9% compared to the LIB with a bare Cu current collector). At a high rate of 1 C, the remaining specific capacity of the LIB with the CC/THCu current collector is better than that with the bare Cu current collector after 200 cycles. The CC/THCu current collector effectively improves the specific capacity and cycle stability of LIBs in contrast to the bare Cu current collector.