Different routes of MgAl–LDH synthesis for tailoring the adsorption of Pb(II) pollutant from water

In this study, new adsorbents based on MgAl-LDHs were synthesized using combined precipitation (co-precipitation) route by modifying temperature and ageing time synthesis parameters, thus tailoring the adsorption capacity of Pb(II) ions from water.The synthesized materials were characterized by SEM, FTIR, XRD and N 2 adsorption-desorption techniques, highlighting the specific lamellar structure of layered double hydroxides (LDHs), as well as the functional groups present on the adsorbent's surface.The maximum adsorption capacity for Pb(II) ions was 1151.97 mg/g for the MgAl-LDH synthesized at 55 °C and aged for 24 h.Sorption of Pb(II) ions occurs not only through co-precipitation in the form of characteristic compounds, Pb(OH) 2 , PbCO 3 or Pb 3 (CO 3 ) 2 (OH) 2 , but also by complexation with surface hydroxyl groups.Résumé.Dans cette étude, de nouveaux adsorbants à base de MgAlLDH ont été synthétisés par voie de co-précipitation en modifiant comme paramètres de synthèse la température et le temps de maturation et utilisés pour contrôller la capacité d'adsorption des ions Pb(II) de l'eau.Les matériaux synthétisés ont été caractérisés par des techniques d'adsorption-désorption de N 2 , SEM, FTIR, XRD, qu'il a mis en évidence la structure lamellaire spécifique des LDH, ainsi que les groupements fonctionnels présents à la surface de l'adsorbant.La capacité maximale d'adsorption des ions Pb(II) était de 1151,97 mg/g pour le MgAlLDH synthétisé à 55 °C et vieilli pendant 24 h.La sorption des ions Pb(II) se fait par précipitation (co-précipitation) sous forme de composés caractéristiques, Pb(OH) 2 , PbCO 3 ou Pb 3 (CO 3 ) 2 (OH) 2 , mais aussi le mécanisme de complexation avec des groupements hydroxyles de surface doit être pris en compte.