Synthesis and Photoluminescence of ZnS Quantum Dots

Single-phase zinc sulphide (ZnS) quantum dots were synthesized by a chemical method. The influence of the pH value of the Zn(CH 3 COO) 2 solution on the size and photoluminescence properties of the ZnS quantum dots was evaluated. X-ray power diffraction, transmission electron microscopy, and ultraviolet-visible spectroscopy were used to characterize the structure, size, surface states, and photoluminescence properties of ZnS quantum dots. The results showed that the crystal structure of ZnS quantum dots was a cubic zinc blende structure, and their average diameter was about 3.0 nm. ZnS quantum dots with good distribution and high purity were obtained. A strong broad band centered at about 320 nm was observed in the excitation spectrum of ZnS quantum dots. Their emission spectrum peaking at about 408 nm, was due mostly to the trap-state emission. The relative integrated emission intensity of ZnS quantum dots decreased as the pH value of the Zn(CH 3 COO) 2 solution increased, which could be ascribed to the increase in average diameter of the ZnS quantum dots as the pH value of Zn(CH 3 COO) 2 solution increased.