Tomáš Kula,Matthias Meiser,R. E. Tressler
标识
DOI:10.1016/0008-8846(80)90093-9
摘要
The effects of curing temperature (21 and 60°C), time (1,7,28 days) and relative humidity (25 to 87%) on the strength and phase compositions of specimens prepared from neat Fondu paste with water/aluminous cement ratio of 0.30 were investigated. The room temperature strengths of the materials aged at 60°C, containing C3AH6 and AH3, were higher than pastes cured at 21°C, containing CAH10. Conversion at 60°C of the specimens aged at room temperature resulted in strengths comparable to materials isothermally cured at 60°C. The effects of these curing conditions on the high temperature strength were also investigated. L'action de la température de durcissement (21° et 60°C), la durée (1, 7, 28 jours) et l'humidité relative sur la résistance et la composition de phase des éprouvettes preparées d'une pâte de rapport eau/ciment alumineux de 0.30 a été étudiée. La résistance, calculée à la température normale d'intérieur, des matériaux âgés à 60°C et contenant C3AH6 et AH3, était plus fortes que la résistance des pâtes âgés à 21°C, contenant CAH10. La conversion à 60°C des éprouvettes âgées a la température normale d'intérieur a obtenu une résistance similaire aux matériaux âgés isothermiquement à 60°C. Les rapports entre les conditions de durcissement et la résistance à haute température ont aussi été etudiés.
科研通智能强力驱动
Strongly Powered by AbleSci AI