Influence of Ni on the Organization and Properties of AlCoCrFeMn High-Entropy Alloys by Laser-Sintering Technique

In order to investigate the effect of the Ni element on the properties of AlCoCrFeMn HEAs, this experiment prepared AlCoCrFeMn and AlCoCrFeNiMn HEAs by using a laser-ignition self-propagation sintering technique with an equal molar ratio. And analyzed the effect of the Ni element on the microstructure of AlCoCrFeMn HEAs by using a metallurgical optical microscope (OM), scanning electron microscope (SEM), energy spectroscopic analysis (EDS), X-ray diffraction (XRD), and other experiments. Characterization equipment was used to analyze the effect of the Ni element on the microstructure, physical phase structure, wear resistance, compressive properties, and corrosion resistance of AlCoCrFeMn HEA materials. The results show that after the addition of the Ni element, the AlCoCrFeNiMn HEA changes from a single BCC phase to one consisting of BCC and a small amount of an FCC phase, with an equiaxial organization, and the yield strength reaches 780 MPa and the compressive strength is 3920 MPa. The corrosion rate is 2.08 × 10−3 mm/a, and the corrosion resistance and mechanical properties are greatly increased.