Spontaneous Formation of Lead‐Free Cs3Cu2I5 Quantum Dots in Metal–Organic‐Frameworks with Deep‐Blue Emission

All-inorganic lead-free Cs3 Cu2 I5 perovskite-derivant quantum dots (QDs) have attracted tremendous attention due to their nontoxicity and unique optoelectronic properties. However, the traditional hot-injection method requires high temperatures and multiple ligands to confine the growth of QDs. Herein, a strategy is reported to spontaneously synthesize ultrasmall Cs3 Cu2 I5 QDs within metal-organic-frameworks (MOFs) MOF-74 at room temperature (RT) with an average diameter of 4.33 nm. The obtained Cs3 Cu2 I5 QDs exhibit an evident deep-blue emission with Commission Internationale de L'Eclairage coordinates of (0.17, 0.07), owing to the strong quantum confinement effect. Due to the protection of MOF-74, the Cs3 Cu2 I5 QDs demonstrate superior stability, and the photoluminescence quantum yield retains 89% of the initial value after the storage of 1440 h under the environment with relative humidity exceeding 70%. Besides, triplet-triplet annihilation upconversion emission is observed within the composite of Cs3 Cu2 I5 @MOF-74, which brings out apparent temperature-dependent photoluminescence. This study reveals a facile method for fabricating ultrasmall lead-free perovskite-derivant QDs at RT without multiple ligands. Besides, the temperature-dependent photoluminescence of Cs3 Cu2 I5 @MOF-74 may open up a new way to develop the applications of temperature sensors or other related optoelectronic devices.