Red mud-metakaolin based cementitious material for remediation of arsenic pollution: Stabilization mechanism and leaching behavior of arsenic in lollingite

The proper treatment of lollingite is of great significance due to its rapid oxidation leading to release of arsenic into the environment. Herein, a green multi-solid waste geopolymer, consisting of red mud, metakaolin, blast furnace slag, and flue gas desulfurization gypsum, was developed. The obtained red mud-metakaolin-based (RMM) geopolymer demonstrated good arsenic retention capability. The results showed that the replacement of SO42- in ettringite with AsO42- via ion exchange, formation of Ca-As and Fe-As precipitates, and physical encapsulation with aluminosilicate gel were the main mechanisms that prevented the release of arsenic. Further dissolution of ettringite in RMM was alleviated by adding a suitable amount of Ca(OH)2 and controlling the pH of the leachate. TCLP results verified that RMM materials possessed an outstanding ability to stabilize arsenic, with a leaching rate below the permitted value of 5 mg/L for safe disposal. The low leachability of the RMM geopolymers (<0.50 mg/L) is potentially related to the pH buffering capacity of the hydration products at a pH range of 2-5. RMM geopolymers showed a high compressive strength (>15 MPa) and low arsenic leaching concentration (<2.66 mg/L) after 28 days of curing. These results demonstrate the potential of RMM geopolymers to be utilized as an environmentally friendly backfilling cementitious material for sustainable remediation of arsenic pollution.