Growth of Atomic layer-deposited Monoclinic Molybdenum Dioxide Films Stabilized by Tin Oxide Doping for DRAM Capacitor Electrode Applications

Dynamic random-access memory (DRAM) capacitor electrodes, exemplified by TiN, face performance limitations owing to their relatively low work functions in addition to the formation of a low-k interfacial layer caused by their insufficient chemical stability. With recent advances in device scaling, these issues have become increasingly problematic, prompting the exploration of alternative electrode materials to replace TiN. Molybdenum dioxide (MoO2) has emerged as a promising candidate for this application, outperforming TiN due to its low resistivity, high work function (>5 eV), and excellent chemical stability. Moreover, monoclinic MoO2 exhibits a distorted rutile structure, enabling the in situ growth of high-k rutile TiO2 on MoO2 at low deposition temperatures. However, MoO2 deposition poses challenges because of its metastable nature compared to the more stable molybdenum oxide (MoOx) phases, such as MoO3 and Mo4O11. In this work, we successfully fabricated Sn-doped MoOx (TMO) films by atomic layer deposition (ALD) at 300 °C. A stabilized monoclinic MoO2 phase was achieved using ALD by incorporating SnOx into MoOx on both SiO2 and TiN substrates. The ALD TMO process comprised MoOx and SnOx subcycles, and the MoOx:SnOx subcycle ratio was varied from 100:1 to 20:1. High growth rates ranging from 0.19 to 0.34 nm/cycle were achieved for ALD TMO with varying the MoOx:SnOx subcycle ratio from 20:1 to 100:0. After post-deposition annealing at 500 °C, polycrystalline TMO films were obtained with smooth surface morphology. ALD TMO exhibited excellent interface quality with ALD TiO2, possessing a negligible low-k interfacial layer. Moreover, a rutile TiO2 film with a high dielectric constant of 136 was successfully grown on a 20% Sn-TMO electrode. Overall, this study provides a strategy to stabilize metastable MoO2 films using ALD, and it demonstrates the superiority of ALD TMO as a promising DRAM capacitor electrode material.