Features of the Process Obtaining of Mg-Zn-Y Master Alloy by the Metallothermic Recovery Method of Yttrium Fluoride Melt

At present, magnesium master alloys with such rare earth metals (REM) as yttrium are used in the production of alloys of magnesium and aluminum. These alloys especially the system Mg-6Zn-1Y-0,5Zr are commonly used in the aircraft and automotive industries. The article is devoted to the exploration of the synthesis process features for ternary magnesium master alloys with yttrium and zinc. The authors used X-ray fluorescence analysis (XRF), differential thermal analysis (DTA), and X-ray spectral analysis (XRD). Optical microscopy was used to conduct microstructural studies. The thermal effects that occur during metallothermic reactions of yttrium reduction from the YF3-NaCl-KCl-CaCl2 salt mixture with a melt of magnesium and zinc were investigated, and the temperatures of these effects were determined. It has been confirmed that the metallothermic reaction of yttrium reduction proceeds from the precursors of the composition: Na1.5Y2.5F9, NaYF4, Na5Y9F32, and KY7F22, and starts at a temperature of 471 °C. The results of experimental studies of the process of metallothermic reduction of yttrium from the salt mixture YF3-NaCl-KCl-CaCl2 are presented in detail. These experiments were carried out in a pit furnace at temperatures ranging from 650 to 700 °C, and it was found that, at a synthesis temperature of 700 °C, the yttrium yield is up to 99.1–99.8%. The paper establishes rational technological regimes for the synthesis (temperature 700 °C, exposure for 25 min, the ratio of chlorides to yttrium fluoride 6:1, periodic stirring of the molten metal) at which the yttrium yield reaches up to 99.8%. The structure of the master alloy samples obtained during the experiments was studied. That structure can be distinguished by a uniform distribution of ternary intermetallic compounds (Mg3YZn6) in the bulk of the double magnesium–zinc eutectic. Studies have been carried out on testing the obtained ternary master alloy as an alloying material in the production of alloys of the Mg-6Zn-1Y-0.5Zr system, while the digestibility of yttrium ranged from 91 to 95%.