Porosity formation studies in high pressure die castings of Al-9Si-3Cu alloy based on Taguchi method

Purpose Nowadays, ample industries are fascinated to look for high strength and light weight materials for the development of robust parts. Because of light weight and high stiffness to weight ratio; usage of aluminum parts is growing rapidly, especially in automotive engineering. Process improvement of Al alloys and their grain structure refinement is the current area of interest in casting companies. In this research work, an investigation has been carried out to enhance the process improvement of die casting by optimization of various significant parameters and their refinement of grains by the effect of Nb-C novel grain refiner. Design/methodology/approach L27 orthogonal array (OA) has been considered to optimize the preferred casting input parameters such as molten metal temperature (°C), die temperature (°C), injection pressure (bar), Al-3.5Nb-1.5 C novel grain refiner and Ni alloying additions as key process parameters in order to increase the quality and efficiency of Al-9Si-3Cu aluminum alloy die casting by reducing the porosity formation. Findings It was observed that the porosity values have significantly decreased from 0.88% to 0.25% particularly at 0.1 wt.% of new grain refiner and 0.5 wt. % of Al-6Ni master alloy. As per the ANOVA results, it was observed that Al-3.5FeNb-1.5 C grain refiner ( F value 2609.22), Al-6Ni alloying addition ( F value 1329.13), molten metal temperature ( F value 1002.43) and, injection pressure ( F value 448.06) are the factors that significantly affects the porosity, whereas die temperature was found to be insignificant. The results show that new grain refiner is one the most significant factor among the other selected parameters. The contribution of the new grain refiner to the variation of mean casting porosity is around 57.74%. confidence interval (CI) has also been estimated as 0.013 for 95% consistency level to validate the predicted range of optimum casting porosity of aforesaid alloy. Originality/value To the best of the authors' knowledge, no study has been conducted in the past to investigate the combined effect of these die casting parameters and composition factors for the development of Al-Si robust cast parts. The paper represents original research and provides new information for the fabrication of die casting parts.