Electrical fatigue behavior of NBT-BT-xKNN ferroelectrics: effect of ferroelectric phase transformations and oxygen vacancies

The reduction of degradation rate at high cycles indicates the subsequent contribution from micro-scale surface damage, leading to irreversible fatigue.